聚甲醛 100TL 美国杜邦 POM Delrin®

性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in2]断裂伸长率
ASTM D638/ISO 527
%拉伸模量
ASTM D638/ISO 5273000kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)
ASTM D638/ISO 527
%拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527
%弯曲模量(弯曲弹性率)
ASTM D790/ISO 1782800kg/cm²(MPa)[Lb/in2]弯曲强度
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in2]洛氏硬度
ASTM D785

IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）
ASTM D792/ISO 11831.43
成型收缩率
ASTM D955
%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133
g/10min220℃/10kgASTM D1238/ISO 1133
g/10min吸水率 23℃/24H
ASTM D570/ISO 62
%热性能热变形温度退火ASTM D648/ISO 75
℃（℉）未退火ASTM D648/ISO 75
℃（℉）维卡软化点
ASTM D1525/ISO R306
℃（℉）熔点
-
℃（℉）燃烧性（率）
UL94

线性膨胀系数
ASTM D696/ISO 11359
mm/mm.℃电气性能介电常数100HZASTM D150/IEC 60250

1MHZASTM D150/IEC 60250

体积电阻率
ASTM D257/IEC 60093
Ω.cm表面电阻率
ASTM D257/IEC 60093
Ω耐电弧性
ASTM D495/IEC 60112

加工条件干燥条件



加工温度射嘴

℃料筒前段

℃料筒中段

℃料筒后段

℃熔体温度


℃模具温度


℃压力注塑压力

Mpa保压压力

Mpa背压

Mpa螺杆转速


rpm其他备注
颜色
特性尺寸稳定性良好 耐磨损性良好用途工程配件 管道 传送机